1. Product Introduction
F150 is a low viscosity fluorine release agent designed for organosilicon pressure sensitive adhesives that require high residual adhesion, and can also be used for pressure sensitive adhesives that are difficult to handle with traditional silicone oil. F-100 crosslinking agent is a special silicone oil crosslinking agent with a wide range of additives, which can effectively balance the two indicators of aging release force and residual adhesion.
2. Product Features
■ The transfer amount of the coating is small, and the residual adhesion is high;
■ Stable release force: 5-10g/25mm;
■ Organosilicon pressure-sensitive adhesives commonly used for BPO curing and some platinum cured organosilicon pressure-sensitive adhesives.
3. Product performance indicators
| Index | F-150 | Crosslinker F-100 |
| Name | Modified polysiloxane | Modified polysiloxane |
| Appearance | Colorless to yellow, transparent to hazy | Transparent liquid |
| Solvent | Heptane | Not |
| Active ingredient（%） | 50 | 100 |
| Viscosity（25℃，cSt） | -- | 20~50 |
4. Usage process and precautions
4.1 Use ratio
F-150: crosslinking agent F-100: catalyst: solvent=100: (1.2-2): (0.5-1.5): 1000. (1) Please adjust the amount of crosslinking agent according to the actual situation; 2. The recommended solvent for the first trial is MIBK: heptane=1:1, and it is not recommended to use a separate solvent, which is easy to produce gel spots or shrinkage pores when using the machine; 3 Properly adding fluorinated solvents, such as HFE 7200 and HFE 7100, can effectively reduce aging release force and improve appearance; 4. Adding tackifiers appropriately can effectively improve the adhesion of the coating
4.2 Process used
Mix F-150 and solvent evenly, add crosslinking agent F-100, and stir for 5-10 minutes; Add platinum catalyst and stir for 5-10 minutes; Add adhesion additives and stir for 5-10 minutes. Recommended temperature and time: 130-180 ℃ (135 ℃: 120s; 160 ℃: 60s)
4.3 Recipe Case
Usage:
| Component Name | Proportion | Coating process |
| F-150 | 100 | |
| F-100 | 2 | |
| Heptane | 500 | 1. Coating of No. 4 wire rod; 2. Curing: 160 ℃, 60s |
| MIBK | 500 | |
| Platinum water 5000ppm | 1 |
Test results:
| Index | Test value |
| Release force（g/25mm） | 5.0 |
| Aging release force, 70℃,24h（g/25mm） | 8.6 |
| Aging release force， 70℃, 7d（g/25mm） | 10.4 |
| Residual adhesion | 100% |
5. Packaging form
F-150 packaging: 0.8kg; 20kg； crosslinking agent
F-100 packaging: 500g; 25kg； catalyzer